A53 A106 Square/Round Cold Rolled Galvanized Steel Pipe

Galvanized Steel Pipe is a kind of Carbon Steel Pipe, mostly Welded Pipe, Galvanized steel pipes are divided into cold galvanized steel pipes (electro galvanized steel pipes) and hot-dip galvanized steel pipes. At present, hot-dip galvanized steel pipes are mainly used in fire protection, electric power and highways.

Galvanizing can increase the corrosion resistance of steel pipes and prolong their service life. Galvanized pipes are widely used. In addition to being used as pipeline pipes for water transmission, gas, oil and other general low-pressure fluids, they are also used as oil well pipes and oil transmission pipes in the petroleum industry, especially in offshore oil fields, as well as pipes for oil heaters, condensing coolers, coal distillation oil washing exchanges of chemical coking equipment, as well as trestle pipe piles, support frames of mine tunnels, etc.

Hot-dip galvanizing (HDG), as referenced is the process of dipping fabricated steel into a kettle or vat of molten zinc.

Hot-dip galvanizing (HDG) is the process of coating iron, steel or ferrous materials with a layer of zinc. This done by passing the metal through molten zinc at a temperature of 860°F (460°C) to form zinc carbonate (ZNC03). Zinc carbonate is a strong material that protects steel and can prevent corrosion in many circumstances. Hot-dip galvanizing can be carried out cheaply and in large batches.

Galvanized Steel Pipe is a welded steel pipe with a hot-dip or electro-galvanized layer on the surface. Galvanizing can increase the corrosion resistance of steel pipes and prolong their service life. Galvanized pipes are widely used. In addition to being used as pipeline pipes for general low-pressure fluids such as water, gas, and oil, they are also used as oil well pipes and oil pipelines in the petroleum industry, especially offshore oil fields, and oil heaters and condensation pipes for chemical coking equipment. Pipes for coolers, coal distillation washing oil exchangers, trestle piles, and support pipes for mine tunnels, etc.

Product Specification

Different processes for Galvanizing metal:

HOT-DIP GALVANIZING

As the name implies, this method involves dipping the base metal into a molten pool of zinc. First, the base metal must be cleaned either mechanically, chemically, or both to assure a quality bond can be made between the base metal and the zinc coating. Once cleaned, the base metal is then fluxed to rid it of any residual oxides that might remain after the cleaning process. The base metal is then dipped into a liquid bath of heated zinc and a metallurgical bond is formed.

The advantages of this method are that it is economical; it can be performed quickly and to complex shapes. However, the final coating can be inconsistent relative to other galvanizing processes.

PRE-GALVANIZING

This method is very similar to hot-dip galvanizing but is performed at the steel mill, usually on materials that already have a specific shape. Pre-galvanizing involves rolling metal sheet through a similar cleaning process to that of the hot-dip galvanizing process. The metal is then passed through a pool of hot, liquid zinc and then recoiled.

An advantage of this method is that large coils of steel sheet can be rapidly galvanized with a more uniform coating compared to hot-dip galvanizing. A disadvantage is that once fabrication of the pre-galvanized metal begins, exposed, uncoated areas will become present. This means that when a long coil of sheet is cut into smaller sizes, the edges where the metal is cut are left exposed.

ELECTRO-GALVANIZING

Unlike the previous processes, electrogalvanizing does not use a molten bath of zinc. Instead, this process utilizes an electrical current in an electrolyte solution to transfer zinc ions onto the base metal. This involves electrically reducing positively charged zinc ions to zinc metal which are then deposited on the positively charged material. Grain refiners can also be added which helps to ensure a smooth zinc coating on the steel. Similar to the pre-galvanizing process, electrogalvanizing is typically applied continuously to a roll of sheet metal.

Some advantages of this process are a uniform coating and precise coating thickness. However, the coating is typically thinner than the coating of zinc achieved by the hot-dip galvanizing method which can result in reduced corrosion protection.

Benefits of galvanized pipe:

Because the pipes are galvanized, it is protected from rust and corrosion. Steel rusts after interacting with water or moisture in the air over time. By adding a coating of zinc to the tubing, galvanized steel round tubing corrodes much slower, extending the life of your tubing.

In addition to this, galvanized pipe also provides:

Lower cost than stainless steel

Lowest long-term cost

Reliable performance

Excellent resistance to mechanical damage

Packaging And Transportation

We offer different modes of transport depending on the customer's destination: rail transport and ship transport，etc.The Shipping Mark shall consist of: Trade mark, Seller's name, Product name, Applicable standards, Specifications, Package No., Contract No., Heat No., Production date, Weighing method, Net weight, Gross Weight, Consignee and Protection symbols, etc.